ANKOR 1126
Hard chromium electrolyte
-------------------ANKOR 1126 硬鉻電解液
CHARACTERISTICS【簡介】
Hard chromium electrolyte with high cathodic current efficiency and good throwing power for the deposition of micro-cracked deposits with a hardness of approximately 1050 HV 0,1. ANKOR 1126 combines the good properties of conventional sulphuric acid electrolytes, i.e. only slight attack of iron and iron alloys and cathodic current efficiencies which are usually only achieved with catalysts on the basis of complexed fluorides. ANKOR 1126 is free of fluorides.硬質鉻電解液具有較高的陰極電流效率和良好的拋擲能力，可沉積硬度約為1050 HV 0,1的微裂紋沉積。ANKOR 1126結合了傳統硫酸電解質的良好性能，即只有輕微的鐵和鐵合金的攻擊和陰極電流效率，這通常只有催化劑在配合氟化物的基礎上實現。ANKOR 1126不含氟化物。
MAKE-UP【組成】
Make up quantities(100 l) 30.00kg Make-up salt ANKOR 1126
5.00 l Make-up solution ANKOR 1126
EQUPMENT【設備】
See Instruction Sheet MB0020"Technical equipment for Chromium electrolytes".
參見說明書MB0020“鉻電解質技術設備”
OPERATING CONDITIONS【操作參數】
Density (20℃) 密度（20℃）
1.215g/cm3
25,5°Be
Temperature 溫度
55-60℃
Current density 電流密度
20-60 A/dm2
Anodic current density 陽極電流密度
15-25 A/dm2
Anode material 陽極材料
The service life of the lead alloy anodes is shorter compared to the service life in chrome plating solutions based on sulphuric acid or mixed and is dependent upon the individual operating conditions. New anodes have to be worked in as described in the Instruction Sheet MB0021 Furthermore platinized titanium anodes are recommended . Care has to be taken that they are completely covered with a lead dioxide film(brown-black layer). Only under this condition is Cr 3+oxidised to Cr6+.The lead dioxide film is obtained using one or more PbSn anodes together with the platinized titanium anodes or by addition of ANKOR Addition Solution PTA (see Technical Data Sheet).與基于硫酸或混合鍍鉻溶液的使用壽命相比，鉛合金陽極的使用壽命較短，并取決于個人的操作條件。新的陽極必須按照說明書MB0021中的描述進行加工。此外，建議使用鍍鉑鈦陽極。必須當心，它們完全覆蓋了一層二氧化鉛薄膜(棕黑色層)。只有在此條件下，Cr3+才被氧化為Cr6+。使用一個或多個PbSn陽極和鍍鉑鈦陽極或通過添加ANKOR添加溶液PTA(見技術數據表)獲得二氧化鉛薄膜。
Voltage電壓
The required rectifier voltage depends on various factors, e.g. current density, concentration, temperature, type of electrode and electrode spacing. Average value: 6 - 12V.所需的整流電壓取決于各種因素，如電流密度、濃度、溫度、電極類型和電極間距。平均值:6 - 12V。
Rectifiers整流器
Usually 12 volt units; for high outputs 15 volt units. 通常是12伏單位;高輸出15伏單位。
Rectifiers have to be adjusted until the residual ripple is less than 5 % within the total current range. 整流器必須調整，直到剩余紋波在總電流范圍內小于5%。
Deposition rate 沉積率
At 50 A/dm2 approx.1,0 um/min chrome is deposited.
MAINTENANCE【維護】
Nominal values